加铁氟龙POM 美国杜邦100AF 高黏度TEFLON3纤维POM
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-792 | 1.54 | ||
| 物理性能 | 扩散因数 | +73℉(+23℃)106Hz | ASTM D-150 | 0.009 | |
| 绝缘系数 | +73℉(+23℃)102;to106Hz | ASTM D-150 | 3.1 | ||
| 电阻系数 | +73℉(+23℃)0.2%H2O | ASTM D-257 | 3×1016 | ohm-cm | |
| 机械性能 | 伸张强度 | +23℃ | ASTM D-638 | 52.4 | MPa |
| 压缩应力 | +23℃@1%Def. | ASTM D-695 | 31.0 | MPa | |
| 拉力冲击抵抗力 | +73℉ | D1822Long | 50 | ft.lb/in2 | |
| 绝缘强度 | Short Time,90 mils | ASTM D-149 | 400(125mils) | V/mil | |
| 压缩应力 | +73°F@1%Def. | ASTM D-695 | 4.5 | MPsi | |
| 压缩应力 | +73°F@10%Def. | ASTM D-695 | 13.0 | MPsi | |
| 弯曲疲劳忍耐限度 | +23℃ | ASTM D-671 | 24.8 | MPa | |
| 挠曲系数 | +158℉ | 在25℃下 | 190 | MPsi | |
| 挠曲系数 | +73℉ | 在25℃下 | 340 | MPsi | |
| 伸张强度 | +212℉ | ASTM D-638 | 4.0 | MPsi | |
| 弯曲降服强 | +23℃ | ASTM D-790 | 72.4 | MPa | |
| Izod冲击强度 | 40℃ | ASTM D-256 | 53.4 | j/m | |
| 弹性系数 | +73℉ | ASTM D-638 | 420 | MPsi | |
| 断裂时之拉力伸张度 | +212℉(+100℃) | ASTM D-638 | 250 | % | |
| 伸张强度 | +100℃ | ASTM D-638 | 28.3 | MPa | |
| 断裂时之拉力伸张度 | +73℉(+23℃) | ASTM D-638 | 22 | % | |
| 拉力冲击抵抗力 | +23℃ | D1822Long | 102 | kj/m2 | |
| 热变形温度 | 66psi | ASTM D-648 | 334 | ℉ | |
| 挠曲系数 | +250℉ | 在25℃下 | 80 | MPsi | |
| 挠曲系数 | +70℃ | 在25℃下 | 1310 | MPa | |
| 电弧抵抗力 | 120mil(3.1mm) | ASTM D-495 | 183no tracking | Sec. | |
| 洛氏硬度 | ASTM D-785 | M78,R118 | |||
| 剪力 | +73℉ | ASTM D-732 | 8.0 | MPsi | |
| 弯曲疲劳忍耐限度 | +73℉ | ASTM D-671 | 3.6 | MPsi | |
| 剪力 | +23℃ | ASTM D-732 | 55.2 | MPa | |
| 挠曲系数 | -68℉ | 在25℃下 | 520 | MPsi | |
| 绝缘强度 | Short Time,2.3mm | ASTM D-149 | 15.8(3.2mm) | MV/m | |
| 伸张强度 | +250℉ | ASTM D-638 | 3.1 | MPsi | |
| 断裂时之拉力伸张度 | -68℉(-55℃) | ASTM D-638 | 15 | % | |
| 伸张强度 | +158℉ | ASTM D-638 | 5.3 | MPsi | |
| 负载下之变形 | 2000psi@+122℉(14Mpa@50℃) | ASTM D-621 | 0.6 | % | |
| 挠曲系数 | +23℃ | 在25℃下 | 2340 | MPa | |
| 挠曲系数 | +122℃ | 在25℃下 | 550 | MPa | |
| 弯曲降服强 | +73℉ | ASTM D-790 | 10.5 | MPsi | |
| 伸张强度 | +122℃ | ASTM D-638 | 20.7 | MPa | |
| Izod冲击强度 | +73℉ | ASTM D-256 | 1.2 | ft.lb/in | |
| 摩擦系数 | +73℉(+23℃)动态 | ThrustWasherTest3 | 0.14 | ||
| 挠曲系数 | +212℉ | 在25℃下 | 110 | MPsi | |
| 断裂时之拉力伸张度 | +158℉(+70℃) | ASTM D-638 | 50 | % | |
| 挠曲系数 | +100℃ | 在25℃下 | 700 | MPa | |
| 伸张强度 | +73℉ | ASTM D-638 | 7.6 | MPsi | |
| Izod冲击强度 | -40℉ | ASTM D-256 | 1.0 | ft.lb/in | |
| 伸张强度 | +70℃ | ASTM D-638 | 36.5 | MPa | |
| 伸张强度 | -68℉ | ASTM D-638 | 10.9 | MPsi | |
| 弹性系数 | +23℃ | ASTM D-638 | 2895 | MPa | |
| 挠曲系数 | -55℃ | 在25℃下 | 3585 | MPa | |
| 压缩应力 | +23℃@10%Def. | ASTM D-695 | 89.6 | MPa | |
| 断裂时之拉力伸张度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| Izod冲击强度 | +23℃ | ASTM D-256 | 64.1 | j/m | |
| 伸张强度 | -55℃ | ASTM D-638 | 75 | MPa | |
| 加工性能 | 吸水量 | 浸泡均衡点+73℉(+23℃) | ASTM D-570 | 0.72 | % |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.18 | % | |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.20 | % | |
| 热性能 | 热变形温度 | 0.5MPa | ASTM D-648 | 168 | ℃ |
| 热变形温度 | 1.8MPa | ASTM D-648 | 118 | ℃ | |
| 线性热膨胀系数 | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 线性热膨胀系数 | -40 to +85℉ | ASTM D-696 | 5.8 | 10-5in/in℉ | |
| 线性热膨胀系数 | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 熔点 | ASTM D-2133 | 347 | ℉ | ||
| 可燃烧性 | UL-94 | 94HB | |||
| 热变形温度 | 264psi | ASTM D-648 | 244 | °F | |
| 线性热膨胀系数 | +85 to +140℉ | ASTM D-696 | 6.8 | 10-5in/in℉ | |
| 熔点 | ASTM D-2133 | 175 | ℃ | ||